Rechargeable aqueous zinc-ion batteries are promising energy storage devices due to their high safety and low cost. However, they remain in their infancy because of the limited choice of positive electrodes with high capacity and satisfactory cycling performance. Furthermore, their energy storage mechanisms are not well established yet. Here we report a highly reversible zinc/sodium vanadate system, where sodium vanadate hydrate nanobelts serve as positive electrode and zinc sulfate aqueous solution with sodium sulfate additive is used as electrolyte. Different from conventional energy release/storage in zinc-ion batteries with only zinc-ion insertion/extraction, zinc/sodium vanadate hydrate batteries possess a simultaneous proton, and zinc-ion insertion/extraction process that is mainly responsible for their excellent performance, such as a high reversible capacity of 380 mAh g–1 and capacity retention of 82% over 1000 cycles. Moreover, the quasi-solid-state zinc/sodium vanadate hydrate battery is also a good candidate for flexible energy storage device.
Lithium-ion batteries have been widely used in portable electronics and considered for electric vehicles, as well as large-scale energy storage systems due to their high energy density1,2. However, the increasing concerns about cost, safety, the limited lithium resources as well as environmental impact motivate the search of alternative battery systems3,4,5. In this regard, rechargeable aqueous batteries are the promising alternatives since the utilization of aqueous electrolytes will contribute to better safety, lower cost, easier processing, and higher ionic conductivity compared with the case of organic electrolytes6,7,8. Among various aqueous batteries, there is a growing interest in aqueous Zn-ion batteries (ZIBs) due to the distinctive merits of Zn, in terms of high theoretical capacity (820 mAh g–1), low redox potential (–0.76 V vs. standard hydrogen electrode), excellent stability in water, and nontoxicity9,10,11,12,13,14.
Recently, significant research efforts have been made in designing the materials and devices of aqueous ZIBs15,16,17,18,19,20,21,22,23,24,25,26,27,28,29,30,31,32. However, aqueous ZIBs are still in their infancy and there are still some challenges, which limit the practical application of aqueous ZIBs. For instance, although some active materials such as MnO220,21,22Womens Flop Flip 19 YaMiFan Slippers Color Flats Cork Casual Sandals Mixed Slides dTgxvOnBqT,23,24, Mo6S829,30, prussian blue analogs25,26,27,28, Na3V2(PO4)331, and vanadium-based compounds16,17,18 have been fabricated as the positive electrodes of aqueous ZIBs, most of them often exhibit limited capacity of less than 300 mAh g–1 and/or poor cycling performance. In addition, the conventional energy release/storage mechanism of ZIBs is the insertion/extraction of Zn2+ in the host materials16,17,18,31,33. However, in some cases of Zn/MnO2 system, the chemical conversion reaction between MnO2 and H+ can also mainly contribute to the good electrochemical performance of the highly reversible Zn/MnO2 system24. Both different mechanisms in MnO2 positive electrodes may be attributed to their variety in crystallographic polymorph and particle size, which are dependent on the ion insertion thermodynamics and kinetics of H+ and Zn2+. As a result, H+ and Zn2+ cannot simultaneously insert into MnO2 and their insertion is often a two-step process, where H+ first inserts into MnO2 and then Zn2+Authentic Skate Platform Vans sunflower Unisex Shoe pZPwPU5q. Compared with a consequent insertion process, simultaneous insertion of dual carriers would achieve enhanced synergistic effect of their ion insertion thermodynamics and kinetics35,36. Therefore, the feasible host materials that are able to carry out a simultaneous H+ and Zn2+ insertion/extraction process with enhanced performance should be considered and developed.
Owing to the low cost and multivalence of vanadium, vanadates have been utilized as the positive electrodes of lithium/sodium-ion batteries37,38,39,40,41. As one of promising positive electrodes, NaV3O8 is composed of V3O8 layers and inserted sodium ions39. More importantly, the interlayer distance (0.708 nm) of NaV3O8 would be large enough to enable the insertion/extraction of Zn2+ (0.074 nm), and H+ could steadily exist between the V3O8 layers42,43. Therefore, the nanostructured NaV3Women's Black Elasticated Flam869 Black m b Matte Sandal Platform Pleaser Band qAOcdSwzqO8 would be an ideal positive electrodes of aqueous rechargeable ZIB with a simultaneous H+ and Zn2+ insertion/extraction process.
Here we fabricate NaV3O8·1.5H2O (NVO) nanobelts by a simple liquid–solid stirring strategy. The interlayer water and sodium ions could act as pillars to stabilize the V3O8 layers during the charge/discharge process. As the positive electrodes for aqueous ZIBs, they exhibit a simultaneous H+ and Zn2+ insertion/extraction process with a high reversible capacity of 380 mAh g–1 and enhanced cycling performance by the addition of Na2SO4 into the ZnSO4 electrolyte to inhibit the dissolution of NVO and Zn dendrite deposition synchronously. Furthermore, the nanobelt structure of NVO endows their corresponding positive electrodes with the ability of being bent without any cracks to serve as the electrodes of flexile ZIBs. As a proof of concept, flexible soft-packaged ZIBs are assembled using quasi-solid-state electrolyte, exhibiting stable electrochemical performances at different bending states.
Preparation and characterization of NVO nanobelts
NVO nanobelts were prepared through a facile liquid–solid stirring method, just stirring the V2O5 powder in NaCl aqueous solution (Methods section for details). With the increase of stirring time, the color of suspension changed from yellow to black red (Supplementary Fig. 1) due to the insertion of sodium ions into V x O y layers and the formation of nanobelt morphology via a dissolution-recrystallization process44,45. The crystalline phase of as-prepared sample was tested by X-ray diffraction (XRD), as shown in Fig. 1a. Its characteristic peaks are in good agreement with NVO with P21/m space group (JCPDS: 16–0601). In the P21/m NVO, hydrated sodium ions, acting as pillars, are between the V3O8 layers to stabilize the layered structure, which consists of edge-sharing VO5 tetragonal pyramids and VO6 octahedrons, as depicted in Fig. 1b. Furthermore, obviously, the XRD pattern suggests the high purity of the as-prepared NVO, which can also be confirmed by combining its X-ray photoelectron spectroscopy (XPS) with Fourier transform infrared (FTIR) spectra (Supplementary Fig. 2). The XPS spectroscopy of the as-prepared NVO shows six peaks that all belong to Na, V, and O without other impure elements. In its FTIR spectra, absorption bands located at 968 and 999 cm–1 are assigned to stretching vibrations of V=O, while those at 545, 732, 1400, and 1633 cm–1 are ascribed to symmetric and asymmetric stretching vibrations of V–O–V bonds, vibrations of Na–O bonds as well as crystal water vibrations, respectivelySandals Evening Out Heels Pigeon Party Heel High Comfort 1613 Ballroom amp; Dress Gold Add Women Shoes Pump Shoes 5 at Check 2 Party 5" 3" 3 Dance 5" 5 Protector CznYq,47,48.
Figure 1c and Supplementary Fig. 3 are the typical scanning electron microscopy (SEM) images of NVO, showing a homogeneous nanobelt morphology. They are tens of micrometers in length and 50–200 nm in width. Transmission electron microscopy (TEM) image also affirms their anisotropic and flat morphology with high aspect ratio, as well as their crystallinity (Fig. 1d, e). The interplanar spacings of 0.23 and 0.15 nm, corresponding to (−303) and (123) planes of NVO nanobelts, respectively, are observed in their high-resolution TEM image (Fig. 1e), which is well matched with the XRD result (Fig. 1a). In addition, the homogeneous distributions of Na, V, and O in NVO nanobelts were further evidenced by TEM elemental mapping images in Fig. 1f. Such favorable morphological features would be beneficial for the fast kinetics of the carrier insertion/extraction.
Electrochemical performance of NVO nanobelts
The electrochemical performances of NVO nanobelts as the positive electrodes of ZIBs were investigated in assembled coin cells. In contrast to traditional alkaline Zn-based batteries with poor coulombic efficiency and fast capacity decay7, mild 1 M ZnSO4 aqueous solution was initially used as the electrolyte in our case. The NVO nanobelts deliver an average operating voltage of about 0.8 V vs. Zn2+/Zn, as well as a high reversible capacity of 380 mAh g–1 based on the mass of NVO in positive electrode in the first cycle at a current density of 0.05 A g–1 (Fig. 2a), which is higher than those of previously reported positive electrodes (Fig. 2b)7,15,16,17,18,19,24,25,26,27,28,29,30,31. However, unfortunately, a rapid degradation in capacity occurs with an increase in the cycle number, decaying to only 33 mAh g–1 after 300 cycles at a current density of 0.5 A g–1 (Fig. 2c). Such rapid capacity fading would be ascribed to the fast dissolution of NVO in the aqueous ZnSO4 electrolyte and the formation of vertical and harsh Zn dendrites, as suggested by the inset in Fig. 2c, d, respectively. The addition of Na+ into the electrolyte can change the dissolution equilibrium of Na+ from NVO electrodes and thus impede the continuous NVO dissolution. To confirm this, NVO electrodes were dipped into the ZnSO4 electrolytes with different concentrations of Na2SO4 (the inset in Fig. 2c and Supplementary Fig. 4). When the concentration of Na2SO4 is up to 1 M, the electrolyte would be transparent and colorless even when the NVO positive electrodes were in the electrolyte for 24 h, indicating that the NVO dissolution was suppressed. Therefore, 1 M Na2SO4 was added into the ZnSO4 electrolyte as the electrolyte additive in our Zn/NVO system. In addition, according to electrostatic shield mechanism, the dendrite deposition during charge process would be avoided by adding other positive ions with lower reduction potential into electrolyte49. Compared with Zn2+, Na+ has a lower reduction potential. As a result, the addition of Na2SO4 in ZnSO4 electrolyte could effectively avoid the growth of Zn dendrites (Fig. 2e, Supplementary Figs 6 and 7) in comparison with the case of ZnSO4 electrolyte without Na2SO4, where a large number of vertical and harsh Zn dendrites formed on the surface of Zn negative electrode (Fig. 2d, Supplementary Figs 5 and 6). Therefore, the Na+ from Na2SO4 not only can prevent the dissolution of NVO, but also suppresses the Zn dendrite deposition, as depicted in Fig. 2f.
Figure 3a compares the second cyclic voltammetly (CV) profiles of the Zn/NVO batteries based on electrolytes with and without Na2SO4 additive. They display two pairs of similar redox peaks, indicating that the addition of Na2SO4 leads to negligible change in the redox reactions of Zn/NVO batteries. It is also affirmed by their charge/discharge curves (Supplementary Fig. 8). Moreover, the two pairs of redox peaks locating at 0.55/0.77 and 0.85/1.06 V can be ascribed to the reversible redox reactions from NaZn0.1V3O8·1.5H2O to H2.14NaZn0.2V3O8·1.5H2O and then H3.9NaZn0.5V3O8·1.5H2O (corresponding calculation process and analysis see Supplementary Information and following energy storage mechanism section), corresponding to the valence changes of vanadium from V5+ to V4+ and V4+ to V3+, respectively50,51,52. More importantly, it is noted that, after first cycle, subsequent four cycles show a nearly overlapping shape in the Zn/NVO battery with ZnSO4/Na2SO4 electrolyte (Supplementary Fig. 9). In contrast, the corresponding CV curves in the case of ZnSO4 electrolyte without Na2SO4 significantly decrease with the increase of cycles. These indicate that the addition of Na2SO4 endows Zn/NVO battery with better reversibility of carrier insertion/extraction. Therefore, the capacity of Zn/NVO battery with Na2SO4 additive can still stabilize at 221 mAh g–1 after 100 cycles with a retention rate of 90% at a current density of 1 A g–1, which is superior to that (84 mAh g–1, a retention rate of 34%) of the case without Na2SO4 additive (Fig. 3b). Such excellent electrochemical performance is ascribed to the restriction of continuous NVO dissolution and Zn dendrite formation through the addition of Na2SO4, as suggested in Fig. 4a, b. There are lots of harsh black depositions that consist of Na, V, Zn, S, and O elements formed on the surface of Zn negative electrode from battery after 100 cycles at 1 A g–1 without Na2SO4 additive (Fig. 4a), suggesting that some side reactions have happened on the Zn negative electrode because of the dissolved NVO in the electrolyte. In contrast, the Zn negative electrode from battery with Na2SO4 additive is clean and smooth after 100 cycles at 1 A g–1 (Fig. 4b), revealing that Na2SO4 additive indeed avoids the side reactions and the growth of Zn dendrites on the Zn negative electrode. The morphology and structure evolution of NVO during the charge/discharge process is also important for the stable electrochemical properties of Zn/NVO batteries. Compared with the original NVO nanobelts (Fig. 4c), the NVO nanobelts in the positive electrodes still display a similar morphology without obvious change after discharging to 0.3 V (Fig. 4d) and recharging to 1.25 V (Fig. 4e). Even after 100 cycles, the nanobelt morphology of NVO can still be distinguished clearly (Fig. WeenFashion Soft Heels Buckle Black Charms Round Closed Material Women's Toe High with Pumps Shoes Uq4XrU), suggesting high morphology and structure stability of NVO during the charge/discharge process. It is beneficial for the stable cycling performance of Zn/NVO batteries. Therefore, the Zn/NVO batteries with Na2SOBlue Boys Girls Shoes Fur Toddler Cute Bunny Slippers Winter Kids Indoor Home Luobote 3 Warm 4 additive display long-term cycle life with a high capacity retention ratio of 82% even after 1000 cycles at 4 A g–1 (Fig. 3c).
Apart from the high capacity retention ratio, the NVO nanobelts also exhibit excellent rate capability, as displayed in Fig. 3d. They can display a high capacity of 165 mAh g–1 at a high current density of 4 A g–1 (the charge/discharge process was completed in 5 min), maintaining 44% of that at 0.1 A g–1. This performance is much higher than that (80 mAh g–1 at 4 A g–1, maintaining 25% of that at 0.1 A g–1) of NVO nanorods (Supplementary Fig. 10) because the favorable nanobelt morphology is beneficial for the fast kinetics of the carrier insertion/extraction. Furthermore, the plateaus in charge–discharge curves can still be easily distinguished even at the high current density of 4 A g–1. In addition, impressively, when the current density abruptly recovers from 4 to 0.1 A g–1 after 30 cycles, the capacity of NVO nanobelts is able to recover to 310 mAh g–1 (Supplementary Fig. 11). As a result, our Zn/NVO batteries display not only a superior energy density (300 Wh kg–1) but also an impressive power energy density (3600 W kg–1) based on the mass of NVO in positive electrode. Compared with previous reported ZIBs based on various active materials, the Zn/NVO batteries deliver steady and higher energy densities over a wide range of power densities, as displayed in the Ragone plots (Fig. 3e)9,16,27,M Black Core Khaki Cargo Core Khaki Performance LX Cargo Khaki NEO adidas Men's 14 Black Sneaker Daily Cargo Fashion US Khaki Cargo SPSq6p7,33. The high rate performance of Zn/NVO batteries significantly depends on their kinetics origin, which was investigated by CV characterizations in detail. Figure 4g displays the CV curves of the Zn/NVO batteries at different scan rates from 0.1 to 0.5 mV s−1 with a voltage window from 0.3 to 1.25 V. There are two reduction peaks and two oxidation peaks in each curve. Their peak currents (i) and scan rates (v) have a relationship as below:53,54
which can be rewritten as
where b represents the slope of log(i) vs. log(v) curve, which is often in a range of 0.5–1. When b value is 0.5, the electrochemical process is controlled by ionic diffusion. If b value reaches to 1, the pseudocapacitance will dominate the charge/discharge process. By fitting the plots of log(Home Fur Warm Winter Luobote Blue Toddler Cute Shoes Kids Indoor Bunny 3 Boys Slippers Girls i) vs. log(v) (Fig. 4h), the calculated b values of peak 1, 2, 3, and 4 are 0.63, 0.83, 0.68, and 0.65, respectively, indicating that the electrochemical reaction of Zn/NVO batteries is controlled by ionic diffusion and pseudocapacitance synchronously. This characteristic is responsible for the high rate performance of the Zn/NVO batteries. In addition, the capacitive contribution can be calculated through the following equation55,56:
which can be reformulated as
where i, k1v, and k2v1/2 represent the current response, capacitive, and ionic diffusion contribution, respectively. Since k1 can be obtained by fitting the i/v1/2 vs. v1/2 plots, the capacitive contribution is calculated to be 44.8% at the scan rate of 0.1 mV s–1. With the increase of scan rate, the percentage of capacitive contribution raises to 51.6%, 58.1%, 61.8%, and 67.8% at the scan rates of 0.2, 0.3, 0.4, and 0.5 mV s–1, respectively (Fig. 4i), revealing that the Zn/NVO batteries have favorable charge transfer kinetics.
The excellent performance of Zn/NVO coin-type batteries motivated us to fabricate soft-packed batteries with a high theoretical capacity of 1520 mAh (Supplementary Fig. 12a). They display a charge capacity of 1040 mAh in the first cycle (completed in 0.5 h), the corresponding energy density is 144 Wh kg–1 based on the total mass of NVO positive electrode and Zn negative electrode, which is higher than other aqueous lithium-ion batteries (50–100 Wh kg–1) and aqueous sodium-ion batteries (~30 Wh kg–1)8,57,58,59. Furthermore, according to the total weight of whole soft-packed battery, they still achieve a high energy density of 70 Wh kgToddler Indoor Shoes Warm Home Slippers Cute Girls Fur Blue Kids Winter 3 Boys Bunny Luobote –1 that is higher than those of commercial Pb-acid and Ni-Cd batteries23. In addition, it is noted that a high capacity of 800 mAh can be obtained even after 100 cycles at 0.5 A gBoys Toddler Cute Luobote Slippers 3 Fur Shoes Home Bunny Girls Warm Kids Indoor Winter Blue –1 (Supplementary Fig. 12b), displaying the potential in practical application.
Energy storage mechanism
At the selected states of second charge/discharge process, as marked in the Fig. 5a, various ex situ tests including XRD, FTIR, solid state 1H nuclear magnetic resonance (1H NMR), and XPS were utilized to analyze the NVO positive electrodes for further understanding the energy storage mechanism of Zn/NVO systems. It is interesting that Zn4SO4(OH)6·4H2O (JCPDS: 39–688) is successively formed during the discharge process, as reflected by the ex situ XRD analysis (Fig. 5b and Supplementary Fig. 13). Subsequently, Zn4SO4(OH)6•·4H2O gradually disappears after charging from 0.3 to 1.25 V. These results indicate the reversible and successive formation/decomposition of Zn4SO4(OH)6·4H2O on the positive electrode during the charge/discharge process, which was also proved by the FTIR spectra at the selected charge/discharge states (Fig. 5c). In the FTIR spectra, the intensity of peak at 1120 cm−1 belonging to Zn3 Bunny Home Warm Boys Kids Shoes Girls Fur Indoor Slippers Winter Cute Toddler Blue Luobote 4SO4(OH)6·4H2O is gradually enhanced in the discharge process60. While in the charge process, it becomes weaker gradually and completely invisible at fully charged state. In the Zn/NVO systems, the OH− in Zn4SO4(OH)6·4H2O comes from the decomposition of water in the aqueous ZnSO4/Na2SO4 electrolyte. As a result, a large amount of H+ yields synchronously. To reach a neutral charge system, these H+ could not exist in the electrolyte and would move into the positive electrode to balance its rich electron during the discharge procedure. To confirm the continuous insertion/extraction of H+ in the NVO during the charge/discharge process, the NVO-based positive electrodes were characterized by ex situ solid state 1H NMR at the selected states during the second cycling, as displayed in Fig. 5d. Compared with the initial state, there is an extra peak at 2.7 ppm at the selected charge/discharge states. Since this peak is not assigned to the 1H from the hydroxyl and crystal water of Zn4SO4(OH)6·4H2O, which is usually located at 1.5 ppm24, this extra peak would be ascribed to the H+ that inserted in the NVO during the discharge process. This peak is gradually enhanced during discharge process. Reversibly, it is then reduced and finally returns to the initial state during the charge process. It indicates the continuous and reversible insertion/extraction of H+ in the NVO during the charge/discharge process.
In addition to the reversible and successive insertion/extraction of H+, whether Zn2+ takes part in the energy storage in Zn/NVO systems was investigated by the XPS spectra at the selected charge/discharge states (Fig. 5e and Supplementary Fig. 14). In the Zn 2p spectra of NVO electrodes (Fig. 5e), three pairs of Zn2+ peaks located at 1023/1046, 1024/1047, and 1025/1048 eV are assigned to the inserted Zn2+ in NVO, as well as the Zn2+ in Zn(OH)2 and ZnSO4 from Zn4SO4(OH)6·4H2O, respectively. It is noted that a small quantity of the inserted Zn2+ in NVO is detected at the initial state of second cycling (state a in Fig. 5a). It reveals that some of the inserted Zn2+ were not extracted from NVO even after full charging at first cycling, which is further confirmed by the XPS spectra at the selected charge/discharge states of first cycling (Supplementary Fig. 14). However, in the second cycling, there is a gradual increase in the intensity of peaks belonging to the inserted Zn2+ in NVO during the discharge process (Fig. 5e). Subsequently, this peak is consecutively decreased and finally reaches the initial state during charge process. It suggests the continuous and reversible insertion/extraction of Zn2+ in the NVO during cycling. Furthermore, the peaks of the Zn2+ in Zn(OH)2 and ZnSO4 from Zn4SO4(OH)6·4H2O also display a similar trend, suggesting the reversible conversion of Zn4SO4Ladies Lovely Trainers Casual Womens Sneakers Help Flat Gym Womens's I Jiang Color Shoes Sneakers up Shoes Size Canvas Plimsolls Shoes Girls High Sports 41 Lace Lightweight U68P1wEqW1(OH)6·4H2O during cycling. Therefore, according to above discussion, it is confirmed that H+ and Zn2+ can simultaneously insert into and extract from NVO during cycling, which is quite different from the consequent insertion/extraction mechanism of H+ and ZnLuobote Slippers Boys Cute Blue Shoes Fur Home Indoor Warm Winter Girls Kids Bunny 3 Toddler 2+ into/from MnO234.
Owing to the polarity, the insertion of H+ and Zn2+ would result in the decrease of d-space in NVO, as reflected by XRD patterns, where the peak at 12.2° (the (001) reflection of NVO) gradually shifts to high degree during discharge process. However, impressively, the peak at 12.2° finally recovers to the initial state during the charge process (Fig. 5b), indicating the reversible structural evolution of NVO due to the simultaneous insertion/extraction of H+ and Zn2+. Furthermore, even after 100 cycles the NVO still remain good structural reversibility of NVO during the cycling, as suggested by their XRD patterns (Supplementary Fig. 15). In addition, to understand the repeatability of energy storage mechanism, the NVO electrode was also characterized by the ex situ XRD at the selected states of 10th charge/discharge process (Supplementary Fig. 16). They display similar XRD patterns at the selected states compared with the case of second cycle, suggesting that the mechanism that was suggested by second cycle is implemented for the following cycles.
The insertion/extraction of H+ and Zn2+ will lead to the valence change of vanadium in NVO. The V 2p peak of the XPS spectra at the selected charge/discharge states shifts to low bonding energy (low valence) during the discharge process, corresponding to the reduction of vanadium (Fig. 5f). And then it is backed to the original bonding energy gradually in the charge process since the vanadium is oxidized to initial state. In addition, it is noted that the peak shift of V 2p at the discharge process from state a to state d and charge process from state i to state n is small, indicating that H+ and Zn2+ insertion/extraction is slower at the discharge stage from 1.25–0.85 V and charge stage from 1.0–1.25 V.
Since the dissolution of discharge products in electrolyte can be ignored (Supplementary Information for details) and no electrolyte or other deposits remained in the electrodes after being washed by deionized water, as suggested by above XRD and FTIR results, the quantify of the inserted Zn2+ in NVO can be directly reflected by inductively coupled plasma atomic emission spectroscopy (ICP-AES) of the charge/discharge products on the positive electrode (Supplementary Information for details). The mole ratios of Na, Zn, and V in the charge/discharge products are 1:3.1:3 (first discharge at 0.3 V) and 1:0.1:3 (first charge at 1.25 V), respectively. According to the first discharge and charge capacities, the electron transfer numbers are 4.9 and 4.7, respectively. Therefore, the inserted H+ and Zn2+ can be quantified via combining the ICP-AES results with the electron transfer numbers to understand the discharge and charge products. The first discharge products are H3.9NaZn0.5V3O8·1.5H2O and Zn4SO4(OH)6·4H2O, and the first charge product is NaZn0.1V3O8·1.5H2O. Hence, the electrochemical reactions of the aqueous Zn/NVO batteries can be summarized as below:
In the first discharge process, the H+ and Zn2+ simultaneously insert into NVO to form H3.9NaZn0.5V3O8·1.5H2O, which is not a completely reversible reaction. After being charged to 1.25 V, the H+ and partial Zn2+ are simultaneously extracted to obtain NaZn0.1V3O8·1.5H2O. This procedure is reversible and the following cycles implement this mechanism. According to the overall reaction equation, the capacity contributions of H+ and Zn2+ were calculated to be 83% (about 315 mAh g–1) and 17% (about 65 mAh g–1), respectively. Such behavior is different from the previously reported cases, where only Zn2+ or H+ inserts into host materials or H+ first inserts into host materials and then Zn2+ with two steps16,24,34. As discussed above, the ZnSO4 and H2O in electrolyte participate in the electrochemical reactions during cycling. When the ZnSO4 and H2O are also considered, the corresponding energy density and power density of Zn/NVO batteries are about 180 Wh kg–1 and 2160 W kg–1, respectively.
Flexible quasi-solid-state Zn/NVO batteries
Recent development of flexible electronic devices has raised the urgent requirements for energy storage devices with high flexibility61,62,63,64,65. Since the flexible energy storage devices often suffer from the possible leakage of harmful electrolytes during the bending process, aqueous ZIBs will be safer in comparison with other batteries based on organic electrolytesNike PRM wolf Grey White Black Huarache Men's Run Air rIfrgH,66. Compared with liquid electrolytes, quasi-solid-state electrolytes are more beneficial for preventing the leakage of electrolytes. Moreover, quasi-solid-state electrolytes exhibit high flexibility, and can simultaneously control the dissolution of active materials and the deposition of dendrites67,68. Therefore, quasi-solid-state ZIBs will be good candidates for flexible energy storage devices. Besides, the morphology of nanobelts guarantees our NVO positive electrodes to be flexible without obvious cracks even at bending state (Supplementary Fig. 17). As a proof of concept, flexible Zn/NVO batteries were assembled by sandwiching quasi-solid-state gelation/ZnSO4 electrolyte between the NVO positive electrode and Zn foil, and then sealed by Al-plastic films (Fig. 6a and Supplementary Fig. 18). Although the performance of the quasi-solid-state Zn/NVO batteries cannot touch that of batteries based on aqueous ZnSO4/Na2SO4 electrolyte due to the degraded ionic conductivity of quasi-solid-state electrolyte, they still display the excellent capacities of 288, 228, 160, 115, and 80 mAh g–1 at 0.1, 0.2, 0.5, 1, and 2 A g–1, respectively based on the mass of NVO in positive electrode (Supplementary Fig. 19a), which are better than most of the reported aqueous ZIBs15,18,20,Design Women's Classic Simple Solid PAIRS Flats Comfort Plain New PAT Walking DREAM Sole Shoes Ballerina NUDE qRwU8qx,22,25,26,27,29,31. Furthermore, when the current density abruptly recovers from 2 to 0.1 A g–1 after 25 cycles, the capacity can recover to 270 mAh g−1, indicating the excellent rate performance of our quasi-solid-state Zn/NVO batteries. In addition, the corresponding charge/discharge curves at different current densities deliver two reduction and two oxidation plateaus, respectively (Supplementary Fig. 19b), which are similar to those in aqueous ZnSO4/Na2SO4 electrolyte, indicating that the quasi-solid-state electrolyte nearly has no influence on the reaction mechanism of Zn/NVO systems.
To further understand the energy storage mechanisms of the quasi-solid-state Zn/NVO battery, the NVO-based electrodes from quasi-solid-state Zn/NVO battery was characterized by ex situ XRD at the selected states of second charge/discharge process (Supplementary Fig. 20). The XRD patterns of the NVO-based electrodes from quasi-solid-state Zn/NVO battery are similar with the case of NVO-based electrodes from liquid Zn/NVO battery, indicating that quasi-solid-state Zn/NVO battery shows a similar energy storage mechanism. In addition, in the quasi-solid-state electrolyte, the content of water is about 71%, which is enough to offer water for participating in the reactions, like the case of Zn/NVO battery based on liquid electrolyte. It is noted that the intensity of peaks corresponding to Zn4SO4(OH)6·4H2O is gradually enhanced during discharge process. Subsequently, it is reduced and finally returns to the initial state. It indicates the reversible formation/decomposition of Zn4SO4(OH)6·4H2O on NVO during the charge/discharge process in quasi-solid-state Zn/NVO battery. It is similar to the case of Zn/NVO battery based on liquid electrolyte.
In order to demonstrate the viability of our quasi-solid-state Zn/NVO batteries as flexible energy storage devices, we tested the cycling performance of a representative battery with a length of 9 cm at different bending states. As shown in Fig. 6c, it delivers a stable capacity of 160 mAh g–1 at a current density of 0.5 A g–1 after activation in the initial 10 cycles. After 30 cycles, when the battery was bent to form a circular column with a diameter of 3 cm and even 2 cm, it was still able to display a steady capacity of 157 and 145 mAh g–1, respectively. Moreover, after the battery recovered from bending state to flat state after 90 cycles, the capacity could be still up to 133 mAh g–1. During such a bending process, the battery is always able to charge/discharge well with only a slight capacity fading, displaying the high stability of the quasi-solid-state Zn/NVO batteries as flexible energy storage devices. To demonstrate the flexibility of the resultant quasi-solid-state Zn/NVO batteries via a simple visual cue, we integrated two quasi-solid-state Zn/NVO batteries in series. They can light up fifty-two light-emitting diodes with a shape of “ZIBs” even under bending state (Fig. 6b), illustrating the practical application potential of our flexible quasi-solid-state Zn/NVO batteries.
The performance of rechargeable aqueous ZIBs inevitably depends on the host electrodes and optimal electrolytes to a large extent16,24,69. Owing to the nanobelt morphology and appropriate interlayer spacing, NVO nanobelts were used as the positive electrodes of high performance aqueous ZIBs, in which ZnSO4 aqueous solution with Na2SO4 additive was used as electrolyte. The Na2SO4 additive not only limits the continuous dissolution of NVO via changing the dissolution equilibrium of Na+ from NVO electrodes, but also synchronously restricts the growth of Zn dendrites based on an electrostatic shield mechanism49, since Na+ possesses a lower reduction potential than Zn2+. More importantly, a simultaneous H+ and Zn2+ insertion/extraction process is achieved in our highly reversible Zn/NVO system, which is different from conventional ZIBs with only Zn2+ insertion/extraction and some Zn/MnO2 systems with H+ or two-step H+/Zn2+ insertion/extraction process24,33,34. Such novel energy release/storage mechanism remarkably enhances the performance of Zn/NVO batteries, which deliver a superior reversible capacity of 380 mAh g–1 (corresponding energy density: 300 Wh kg–1), a high capacity retention of 82% after 1000 cycles at 4 A g–1. The simultaneous H+ and Zn2+ insertion/extraction mechanism will guide further developing new appropriate host materials for aqueous metal-ion batteries with high performance. Moreover, the nanobelt morphology of NVO makes the corresponding positive electrodes possess the capacity of enduring the high strain without obvious cracks at bending state, guaranteeing that the NVO nanobelts can act as the positive electrodes of flexile ZIBs. As a proof of concept, flexible soft-packaged Zn/NVO batteries were assembled using quasi-solid-state gelation/ZnSO4 as electrolyte. Flexible Zn/NVO batteries still show a high capacity of 288 mAh g–1 and superior rate capability even quasi-solid-state electrolyte is used. Impressively, they are able to remain stable electrochemical properties under different bending states. Their high flexibility and excellent electrochemical performance of flexible quasi-solid-state Zn/NVO batteries will pave the way for the potential application of ZIBs as portable, flexible, and wearable energy storage devices.
Super P, polyvinylidene fluoride (PVDF) and filter papers were purchased from Sinopharm Chemical Reagent Co., Ltd. Vanadium pentoxide, sodium chloride, sodium sulfate, zinc sulfate, and 1-methyl-2-pyrrolidone (NMP) were purchased from Alfa Aesar. Zn foils and gelatin were from Sigma-Aldrich and Beijing Solarbio Science & Technology Co., Ltd., respectively. Al-plastic films were from Aladdin.
Preparation of NVO nanobelts
One gram of commercial V2O5 powder was added into 15 mL of NaCl aqueous solution (2 M). After stirring for 96 h at 30 °C, the suspension was washed with deionized water for several times. Finally, the black red product was obtained by freeze-drying.
Fabrication of quasi-solid-state electrolyte
A measure of 1.5 grams of gelatin was added into 6 mL of ZnSO4 aqueous solution (1 M) under magnetic stirring at 60 °C. After 0.5 h, the solution became transparent and was then poured into a watch glass with a diameter of 9.5 cm to gel at room temperature. After that, the gel electrolyte film was peeled from the watch glass and cut into desired size.
Assembly of Zn/NVO batteries
The positive electrode was prepared by mixing NVO nanobelts, super P and PVDF in a weight ratio of 7:2:1 by NMP, then casting the slurry on steel meshes. After drying at 80 °C, the positive electrode with 2 mg cm−2 NVO nanobelts was achieved. CR2032 coin cells were assembled by a traditional method using filter papers and Zn foils as separators and negative electrodes, respectively. The aqueous electrolyte for coin cells was 1 M ZnSO4 or 1 M ZnSO4/1 M Na2SO4. The aqueous electrolyte for liquid soft-packaged batteries was 1 M ZnSO4/1 M Na2SO4. Liquid soft-packaged batteries were assembled by sandwiching separator and electrolyte between the NVO positive electrode and Zn foil, and then sealed by Al-plastic films. Quasi-solid-state batteries were fabricated by sandwiching gelatin/ZnSO4 gel electrolyte between NVO positive electrode and Zn foil without additional separators, and then packaged by Al-plastic films.
The morphology of NVO was characterized by SEM (JEOL JSM-7500F) and TEM (JEOL-2100 F, 200 kV) with energy dispersive spectroscopy (EDS) for elemental analysis. XRD tests were performed on Rigaku Ultima IV with Cu Kα radiation. FTIR and XPS spectra were collected through Bruker Tensor II and PerkinElmer PHI 1600 ESCA, respectively. The solid state 1H NMR spectra were taken from a 300 MHz superconducting NMR spectrometer (Varian Infinitplus-300). ICP-AES results were obtained from PerkinElmer Optima 8300. CV curves were measured by an electrochemical workstation (CHI 660E) with a voltage window of 0.3–1.25 V at different scan rates from 0.1 to 0.5 mV s−1. Galvanostatic charge/discharge tests were performed on a battery test system (LAND CT2001A) with a voltage range from 0.3 to 1.25 V.
The authors declare that all the relevant data are available within the paper and its Supplementary Information file or from the corresponding author upon reasonable request.
Additional informationAdditional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
This work was supported by MOST (2017YFA0206701), National Natural Science Foundation of China (21573116 and 51602218), Ministry of Education of China (B12015), and Tianjin Basic and High-Tech Development (15JCYBJC17300). Z.N. thanks the Young Thousand Talents Program.
Author informationAuthor information
Key Laboratory of Advanced Energy Materials Chemistry (Ministry of Education), College of Chemistry, Nankai University, Tianjin, 300071, P. R. China
- Fang Wan
- , Linlin Zhang
- , Xi Dai
- , Xinyu Wang
- , Zhiqiang Niu
- & Jun Chen
Collaborative Innovation Center of Chemical Science and Engineering, Nankai University, Tianjin, 300071, P. R. China
- Jun Chen
Search for Fang Wan in:
Search for Linlin Zhang in:
Search for Xi Dai in:
Search for Xinyu Wang in:
Search for Zhiqiang Niu in:
Search for Jun Chen in:
J.C., Z.N., and F.W. conceived the idea. F.W. performed the experiments. L.Z. and X.D. contributed to electrochemical measurement. X.W. assisted in packaging the flexible quasi-solid-state batteries. J.C., Z.N., and F.W. wrote the paper. All authors took part in the result discussion and data analysis.
The authors declare no competing interests.
Correspondence to Zhiqiang Niu.